Method of growing semiconductor heterostructures based on gallium nitride

ABSTRACT

The method of growing non-polar epitaxial heterostructures for light-emitting diodes producing white emission and lasers, on the basis of compounds and alloys in AlGaInN system, comprising the step of vapor-phase deposition of one or multiple heterostructures layers described by the formula Al x Ga 1-x N(0&lt;x≦1), wherein the step of growing A 3 N structures using (a)-langasite (La 3 Ga 5 SiO 14 ) substrates is applied for the purposes of reducing the density of defects and mechanical stresses in heterostructures.

FIELD OF THE INVENTION

The invention is related to methods of manufacturing of semiconductor materials and devices, and more particularly, to manufacturing non-polar epitaxial heterostructures of third group elements nitrides (further A³N structures) by Organometallic Vapor-Phase Epitaxy (further OMVPE) which are usually used for such devices, as lasers, light emitting diodes (LEDs), and particularly, white LEDs.

DESCRIPTION OF THE RELATED ART

A³N semiconductor heterostructures are basic materials for design and manufacture of high efficient light emitting diodes and lasers in visible and ultraviolet parts of optical spectrum of radiation, including white LEDs.

In the reference [1] use of converting dark blue and/or ultra-violet radiation of GaN-mis structures into longer wavelength radiation in visible part of spectrum with the help of covering these structures by stocks phosphors was offered for the first time.

In the reference [2] design of white light emitting diodes on the basis of dark blue p-n AlGaInN heterostructure emitters covered by Yttrium-Aluminum-Garnet phosphor has been offered. Part of the primary dark blue radiation of emitters is converted into yellow radiation of phosphor. As a result, mixing of blue radiation from an emitter and complementary yellow luminescence exited by the blue radiation in phosphor produce white light by LEDs with certain coordinates of chromaticity.

Three basic designs of white light-emitting diodes essentially differing from each other are known:

-   -   light-emitting diodes on the basis of an emitter of dark blue         color of luminescence which is covered by a layer of stocks         phosphor converting a part of dark blue radiation into yellow         radiation;     -   light-emitting diodes on the basis of an emitter of ultraviolet         radiation which is covered by a layer of stocks phosphor         converting ultraviolet radiation into red, green and dark blue         bands of luminescence (RGB system);     -   full-color light-emitting diodes containing three separate         emitters radiating in red, green and dark blue parts of spectrum         (RGB system).

Despite of distinction, improvement of parameters of all listed types of white light-emitting diodes demands perfection of methods of epitaxial A³N-heterostructures growth and increase of quantum output of radiation of phosphors.

For mass production of light emitting diodes the most preferable method of manufacturing A³N-heterostructures is the method of Organometallic Vapor-Phase Epitaxy (OMVPE).

Sapphire (Al₂O₃), silicon carbide (6H—SiC), gallium nitride (GaN) and aluminum nitride (AlN) are used as substrates for A³N epitaxial structures growth. Cheaper sapphire substrates are most of all used. Silicon carbide substrates in some times more expensive than sapphire ones and, therefore, are used not so often. Close to ideal there could be substrates made of GaN or AlN, but their mass production is not achieved yet.

Typical A³N-heterostructures for light-emitting diodes contain following functional parts:

-   -   a single crystal substrate of sapphire or silicon carbide which         surface is crystallographic c-plane (0001) defining         crystallographic type of A³N epitaxial layers, for example,         wurtzite type of their crystal structures and azimuthally         orientation of crystallographic lattices;     -   wide-bandgap emitters, as a rule, n-type and p-type         Al_(X)Ga_(1-X)N layers providing effective injection of         electrons and holes and their confinement in active region of         the heterostructure;     -   an active region containing, as a rule, a set of narrow-bandgap         layers of such materials, as In_(X)Ga_(1-X)N alloys which are         usually not specially doped;     -   contact epitaxial GaN layers of n-type and p-type conductivity         providing low specific resistance of ohmic contacts and uniform         distribution of current density in a cross-section of a device.

In A³N-epitaxial heterostructures used in various devices, in particular in light-emitting diodes and lasers, density of defects (dislocations, defects of packing, etc.) and also a level of mechanical stresses should be as low, as possible. For example, GaAs laser heterostructures usually have dislocation density not exceeding values of 10²-10³ cm⁻².

In A³N-heterostructures basically exists two sources of defects, first of which concerns to a difference of lattice parameters of a substrate and A³N epitaxial layers and second one concerns to a mismatch of lattice parameters of layers inside of a heterostructure, for example, between GaN and Al_(X)Ga_(1-X)N layers or between GaN and In_(X)Ga_(1-X)N layers. In the case of GaN or AlN substrates the contribution of the first defects source is decreasing and is comparable with the second defects source contribution.

A³N single-crystal epitaxial layers which have wurtzite type of crystal structure: AlN (lattice parameter a=0.311 nm), GaN (a=0.316 nm) and InN (a=0.354 nm), grown on single-crystal Al₂O₃ substrates oriented in (0001)-plane (the oxygen sublattice parameter a=0.275 nm) or on 6H—SiC substrates (a=0.308 nm), always contain high density of defects, basically dislocations.

Dislocations are formed in interface “substrate—epitaxial layer” because there is an essential difference of lattice parameters of a substrate and a epitaxial layer. Lattice parameters of epitaxial layers are larger than a lattice parameter of a substrate (discrepancy up to 16%) and dislocations will spread through heterostructure layers. In typical AlGaInN heterostructures used in blue and green light-emitting diodes, which have been grown on sapphire substrates, dislocation densities may have values 10⁸-10¹⁰ cm⁻². For similar heterostructures grown on SiC substrates dislocation densities may have values 10⁷-10⁹ cm⁻². Thus, the contribution of the first source of defects is defined by a value 10⁷-10⁹ cm⁻², the contribution of the second source of dislocations formation inside a heterostructure is equal to 10⁶-10⁷ cm⁻². In particular, formation of high density of dislocations and even cracking AlGaN layers is caused by a difference of lattice parameters of GaN and AlN layers (discrepancy of 3.5%) and by their differences in thermal expansion coefficient values.

For the partial solution of these problems can be used methods. In first of them before growing a AlGaN layer, for example, n-type emitter layer, a thin In_(0.1)Ga_(0.9)N layer is grown (thickness about 0.1 microns) to prevent cracking a subsequent Al_(X)Ga_(1-X)N (x=0.15-0.20) layer. In the second method instead of a bulk Al_(X)Ga_(1-X)N n-type emitter layer with a constant x-value a strained multiquantum superlattice AlGaN/GaN layer is grown. The thickness of each layer in the superlattice is about 0.25 nm.

A very special feature of Organometallic Vapor-Phase Epitaxy for A³N-heterostructures growth is necessity of abrupt changing temperature of substrates during a technological process. So, at growing a buffer layer (usually a very thin amorphous GaN or AlN layer) the temperature of sapphire or silicon carbide substrates is rapidly decreased from 1050° C.-1100° C. down to 550° C. and after finishing the amorphous GaN or AlN layer growth the substrate temperature is rapidly increased up to the temperature of growth of a single crystalline GaN layer (1050° C.). If process of heating substrates with a buffer GaN or AlN layer is slow, it will lead to crystallization of a thin (about 20 nm) GaN layer and subsequent growing a thick GaN layer leads to formation of a nonplanar film which has great number of defects and figures of growth.

Another necessity of change of substrate temperature during growth is realized at growing In_(X)Ga_(1-X)N layers (at x>0.1) in active region of the heterostructure. These layers have a tendency to thermal decomposition at temperatures above 850° C.-870° C. In this case growing In_(X)Ga_(1-X)N layers is completed at a lower (800° C.-850° C.) temperature. During increasing the substrate temperature up to 1000° C.-1050° C. the process of heterostructure growth should be interrupted by disconnecting submission of metalloorganic Ga, Al and In precursors to substrates. With the purpose to exclude thermal decomposition of In_(X)Ga_(1-X)N layers they are sometimes covered with a thin (˜20 nm) protective Al_(0.2)Ga_(0.8)N layer. This layer has sufficient stability to dissociation up to temperatures about 1050° C. Sharp change of temperature of a substrate with deposited epitaxial layers (except during a GaN or AlN buffer GaN layer growing) can lead to additional formation of defects and cracking grown layers, for example, AlGaN layers. Thus, it is desirable to have such methods of A³N-heterostructures growth, in particular structures for super bright light-emitting diodes, which allow smooth change of growth temperatures and exclude interruptions of a growth process at In_(X)Ga_(1-X)N layers growing. These methods of growth have also to reduce density of dislocations generated in interfaces of A³N heterostructure layers. Reduction of dislocations penetrating into a (0001) heterostructure grown on sapphire or silicon carbide substrates can be achieved by use of special techniques including lateral epitaxial overgrowth (LEO-technology). At first, in this technology a thin buffer GaN layer is usually grown at a low temperature. Then a SiO₂ or Si₃N₄ film is deposited on the structure surface. In this film narrow long parallel each other windows are etched down to the buffer layer and then, during the next epitaxy process, a thick GaN layer has been grown on SiO₂ or Si₃N₄ film surface at a high temperature. In the same process a A³N heterostructure is also grown up. It is easy to see, that the LEO-technology is much more complex and more labor-consuming, than usual technology.

Theoretical and, partially, experimental investigations predict advantage of use non-polar a-plane (further a-A³N) heterostructures in a lot of devices, in particular, in light-emitting diodes and lasers. In comparison with usual polar heterostructures grown along the polar c-direction [0001] in a-A³N non-polar heterostructures strong electrostatic fields along the direction of growth are absent. Owing to it, spatial separation of injected electrons and holes in the active region of non-polar a-A3N heterostructures is eliminated and, as consequence, increase of internal quantum efficiencies of radiation in light-emitting diodes and lasers made on their basis can be expected.

A lot of publications is devoted to growth of a-A³N non-polar heterostructures. In the patent application [3] growth of a-GaN (1120) films on r-plane (1102) sapphire substrates is described. In the publication [4] advanced a-A³N non-polar heterostructures grown on a-GaN substrates are proposed by Sh. Nakamura.

At last, in the patent application [3] the opportunities of a-A³N non-polar heterostructures growth on silicon carbide, silicon, zinc oxide, lithium aluminates, lithium niobate and germanium substrates are mentioned.

Thus, a-A³N non-polar heterostructures growth providing low dislocations and structural defects densities is rather actual direction of technology developments to solve problems of increasing internal quantum efficiencies of light-emitting diodes and lasers and their life-times.

THE BRIEF DESCRIPTION OF THE INVENTION

The subject of this invention is a new method of growing non-polar a-A³N epitaxial homo- and/or heterostructures on the basis compounds and alloys in AlInGaN system on which have low dislocations and structural defects densities in layers on LANGASITE (a-La₃Ga₅SiO₁₄) substrates instead substrates made of other known materials to use these A³N-structures in design and manufacturing light-emitting diodes and lasers. The properties of A³N materials and langasite are presented in Table 1.

According to the first aspect of the invention a method of growth in which for decreasing dislocations density at the interface “the first epitaxial Al_(x)Ga_(1-X)N layer—the substrate” and in other functional layers of light-emitting heterostructure a-langasite substrate is used. Mismatch of c-lattice parameters of the substrate and the first epitaxial Al_(x)Ga_(1-X)N layer is no more than within the limits from −2.3% at x=1 up to +1.7% at x=0, and mismatch of their thermal expansion coefficients in the direction along the c-axis is no more than within the limits from +46% at x=1 up to 31 15% at x=0. Thus, there are particular x-values at which mismatch of c-lattice parameters of the substrate and the first epitaxial Al_(x)Ga_(1-X)N layer and mismatch of their thermal expansion coefficients in the direction along the c-axis are absent (Table 1).

In conformity with the second aspect of the invention, for manufacturing a “white color heterostructure with built-in phosphor” the langasite substrate is doped by special impurities to convert part of the primary dark blue radiation of the A³N heterostructure (λ_(MAX)=455 nm) into yellow radiation of the substrate, thus the substrate structure corresponds to formula La_(3-x-y)Ce_(x)Pr_(y)Ga₅SiO₁₄.

According to the third aspect of the invention, a topology of the langasite substrate and a design of the emitter chip are offered, at that all dark blue radiation of heterostructure is directed into the substrate to increase radiation power and to achieve uniform spatial distribution of color temperature of white radiation.

TABLE 1 Physical A³N type nitrides Langasite properties AlN GaN InN Al_(0.44)Ga_(0.56)N La₃Ga₅SiO₁₄ Crystal wurtzite wurtzite wurtzite wurtzite Trigonal structure group P321 Lattice 3.112 3.189 3.548 3.155 8.173 constant a, Å (direction perpendicular to c- axis) Lattice 4.982 5.185 5.760 5.099 5.099 constant c, Å (direction parallel to c-axis) Ratio of lattice 0.977 1.017 1.130 1.00 — constants (−2.3%) (+1.7%) (+13%)  (0%) c_(A3N)/c_(La3Ga5SiO14) Thermal expansion 5.3 × 10⁻⁶ 3.17 × 10⁻⁶ 3.0 × 10⁻⁶ 4.11 × 10⁻⁶ 3.56 × 10⁻⁶ (Δc/c), K⁻¹ (direction parallel to c-axis) Thermal expansion 4.2 × 10⁻⁶ 5.59 × 10⁻⁶ 4.0 × 10⁻⁶ 4.98 × 10⁻⁶ 5.11 × 10⁻⁶ (Δa/a), K⁻¹ (direction perpendicular to c- axis) Ratio of thermal 1.49 0.89 0.84 1.15 — expansion coefficients  (+49%)  (−11%) (−16%) (+15%) (Δc/c)_(A3N)/ (Δc/c)_(La3Ga5SiO14) (direction parallel to c-axis)

THE BRIEF DESCRIPTION OF DRAWINGS

The drawings included in this application provide detailed description of advantages of the invention and help to understand its essence. Similar reference numbers represent corresponding parts throughout.

FIG. 1 is a drawing of a polar light-emitting A³N-heterostructure grown by a usual method of epitaxy—prototype [2].

FIG. 2 is a drawing of a non-polar light-emitting A³N-heterostructure grown on a langasit substrate.

FIG. 3 is a schematic view of a light-emitting heterostructure on a langasite substrate with an additional Ce- and Pr-doped langasite layer grown on the surface of the A³N-heterostructure.

FIG. 4 represents an emission spectrum produced by the light-emitting diode on the Ce- and Pr-doped langasite substrate.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is described below with references to drawings.

FIG. 1 represents a typical light-emitting diode heterostructure and changing bandgap energy in heterostructure layers corresponding to prototypes; U.S. Pat. No. 5,290,393 March 1994, Nakamura; U.S. Pat. No. 5,993,542 November 1999, Yanashima; U.S. Pat. No. 5,909,036 June 1999 Tanakana. This heterostructure contains an additional n-In_(X)Ga_(1-X)N layer (4) grown to prevent cracking a following n-AlGaN (5) emitter layer which is grown before a multiple quantum wells In_(X)Ga_(1-X)N/In_(y)Ga_(1-Y)N active layer (6).

FIG. 2 represents a light-emitting diode heterostructure, grown on a langasit substrate. A profile of changing bandgap energy in different heterostructure layers is also shown. Unlike the structure represented in FIG. 1 in the offered structure the n-In_(X)Ga_(1-X)N layer (4) and the p-GaN layer (8) are not grown. The p-GaN layer (8) is a wave guiding layer which is most effectively used in laser diodes, not in light-emitting diodes. For growth of a light-emitting diode heterostructure a langasit substrate (1) having the a-plane orientation and perfect surface treatment (Ra<0.5 nm) is loaded into a reactor of an OMVPE apparatus in very clean nitrogen atmosphere conditions. After blowing through the reactor by pure nitrogen hydrogen pressure in the reactor decreases to an operating level nearby 70 Torr. Then the graphite susceptor with the substrate are heated up to 1050° C. After heating during 15 min at hydrogen flow rate of 15 liter/min ammonia with flow rate of 5 liter/min is supplied into the reactor. In this condition the process is sustained for 5 minutes. After that high-frequency heating power is decreased and within 6 minutes the temperature of the susceptor is stabilized at the level 530 ° C.

Then, to grow up a GaN buffer layer (2) trimethylgallium (TMG), as the source gas, with flow rate of 4*10⁻⁵ mol/min is supplied through separate injection nozzle into the reactor for 50 seconds. As a result, the GaN buffer layer with thickness of 15 nm is grown. After that, the susceptor temperature is very rapidly risen up to 1030° C. and TMG with silane (SiH₄) used as a donor impurity source is supplied into the reactor with flow rate of 7*10⁻⁵ mol/min. The TMG+SiH₄ gas mixture has flow rate of experimentally selected value to have a doping level of the GaN layer about 2*10¹⁸ cm⁻³. The GaN layer (3) with thickness about 3.2 microns grows for 35 minutes. Then the trimethylaluminum (TMAl) is supplied as a source gas, and its flow rate linearly increases from 0 to 1*10⁻⁵ mol/min during 5 minutes. As a result, the n-Al_(x)Ga_(1-x)N (x<0.15) (5) layer with thickness of 0.5 microns and with a gradient of aluminum content is grown. After that, supplying TMG, TMAl and SiH₄ is stopped, the susceptor temperature has been very rapidly reduced down to 860° C. during 5 minutes. Now, submission of TMG and trimethylindium (TMI) is switched on and growth of In_(x)Ga_(1-x)N/In_(y)Ga_(1-y)N layers (6) forming a multiple quantum wells structure occurs by periodically switching TMI flow rates between 7*10⁻⁶ mol/min and 3*10⁻⁵ mol/min. Duration of TMI submission with the higher flow rate takes of 3 seconds and with the lower flow rate of 16 seconds. Then the susceptor temperature rises up to 1030° C. during 5 minutes and TMG+TMAL flows are supplied into the reactor again. During growth of AlGaN (9) and GaN (10) layers bis(cyclopentadienyl)magnesium (Cp₂Mg) as a source of acceptor impurity is supplied into the reactor. The Cp₂Mg flow rate must be high enough to obtain the acceptor concentration of the order 3*10¹⁸ cm⁻³ for providing low specific resistance of the p- GaN contact layer (10).

In FIG. 3 a design of an emitter for an white light-emitting diode is represented. The emitter consists of a heterostructure radiating in dark blue part of spectrum whose layers (2)-(10), according to the invention, are grown on a-langasite substrate by selective OMVPE epitaxy. The langasite composition is described by formula La_(3-x-y)Ce_(x)Pr_(y)Ga₅SiO₁₄. There are specially prepared recesses in the substrate for selective heterostructure epitaxy. Before the final operation of separating a wafer into chips there are made a number of technological operations: photolithography, removal of layers (6), (9) and (10) from part of the selectively grown heterostructure by etching, deposition of the reflecting coating (11) consisting of thin layers of nickel and gold, and deposition of the ohmic contact (12) layer consisting of the tin-gold alloy which is needed for the subsequent mounting the emitter on the base of a light-emitting diode. Absorption of the dark blue radiation of the heterostructure excites yellow photoluminescence in the substrate, caused by presence of Ce and Pr in langasite. Effective transformation of part of dark blue radiation into yellow is provided with absence of air interlayer between the selectively grown heterostructure and langasite surrounding it from the all directions. As a result, due to mixture of dark blue and yellow radiation the emitter generates white light.

In FIG. 4 a typical design of a white light-emitting diode (prototype) is represented in which a dark blue color emitter (13) is used covered by usual Yttrium-Aluminum-Garnet phosphor (14).

INDUSTRIAL APPLICABILITY

A³N-heterostructures on a-plane langasite substrates grown by the method proposed in the invention have lower density of defects than structures by usual methods and have no microcracks. The dislocation density in heterostructures represented in the FIG. 2 may have values less than 5*10⁷ cm⁻². Emitters have white color of light with chromatic coordinates X=0.31, Y=0.31.

[1] SU No 635813, 7 Aug. 1978.

[2] U.S. Pat. No. 5,998,925, 7 Dec. 1999.

[3] M. Craven et al, Dislocation reduction in non-polar gallium nitride thin films, PCT/US03/11177, 15 Apr. 2003.

[4] Sh. Nakamura, Growth and device strategies for AlGaN-based UV emitters, UCSB, 2004. 

1. A method of growing non-polar A³N epitaxial heterostructures for light-emitting diodes producing white light emission and lasers, on the basis of compounds and alloys in an AlGaInN system, the method comprising: vapor-phase depositing at least one A³N heterostructure layer comprising the formula Al_(x)Ga_(1-x)N (0<x≦1) on an (a)-langasite (La₃Ga₅SiO₁₄) substrate; and growing a phosphor-doped (a)-langasite layer on the surface of the at least one A³N heterostructure, wherein vapor-phase depositing the at least one A³N heterostructure using an (a)-langasite (La₃Ga₅SiO₁₄) substrate reduces defect density and mechanical stresses in the A³N heterostructures.
 2. The method of claim 1, wherein the (a)-langasite substrate comprises the formula La_(3-x-y)Ce_(x)Pr_(y)Ga₅SiO₁₄ (x=0.1±3%, y=0.01±1%), the (a)-langasite substrate used as the substrate for growing the at least one A³N heterostructure, the (a)-langasite substrate to transform a part of blue wavelength radiation emitted by the at least one A³N heterostructure into a yellow wavelength.
 3. The method of claim 1, wherein the (a)-langasite substrate is used as a substrate for growing a non-polar A³N heterostructure for a green wavelength or ultraviolet wavelength radiation device.
 4. The method of claim 1, wherein a phosphor doped (a)-langasite substrate is used as a substrate for growing a non-polar A³N heterostructure, the phosphor doped (a)-langasite substrate for transformation of ultraviolet wavelength radiation into visible wavelength radiation, including white light.
 5. The method of claim 1, wherein the thickness of the (a)-langasite substrate is less than or equal to 80 microns.
 6. The method of claim 1, wherein the (a)-langasite substrate comprises a Ce-doped or a Pr-doped langasite buffer layer deposited on a material of the group comprising at least one of Si, Al₂O₃, Ge or similar materials.
 7. A method of growing non-polar A³N epitaxial heterostructures for light-emitting diodes producing white light emission and lasers, on the basis of compounds and alloys in an AlGaInN system, the method comprising: vapor-phase depositing at least one A³N heterostructure layer comprising the formula Al_(x)Ga_(1-x)N (0<x≦1) on an(a)-langasite substrate; and growing a phosphor-doped (a)-langasite layer on the surface of the at least one A³N heterostructure, wherein vapor-phase depositing the at least one A³N heterostructure using an (a)-langasite (La₃Ga₅SiO₁₄) substrate is applied to reduce defect density and mechanical stresses in the A³N heterostructures, and wherein the thickness of the phosphor-doped (a)-langasite layer is less than or equal to 3 microns.
 8. The method of claim 7, wherein the (a)-langasite substrate comprises the formula La_(3-x-y)Ce_(x)Pr_(y)Ga₅SiO₁₄ (x=0.1±3%, y=0.01±1%), the (a)-langasite substrate used as the substrate for growing the at least one A³N heterostructure, the (a)-langasite substrate to transform a part of blue wavelength radiation emitted by the at least one A³N heterostructure into a yellow wavelength.
 9. The method of claim 7, wherein the (a)-plane langasite substrate is used as a substrate for growing a non-polar A³N heterostructure for a green wavelength or ultraviolet wavelength radiation device.
 10. The method of claim 7, wherein a phosphor doped (a)-langasite substrate is used as a substrate for growing a non-polar A³N heterostructure, the phosphor doped (a)-langasite substrate for transformation of ultraviolet wavelength radiation into visible wavelength radiation, including white light.
 11. The method of claim 7, wherein the thickness of the (a)-langasite substrate is less than or equal to 80 microns.
 12. The method of claim 7, wherein the (a)-langasite substrate comprises a Ce-doped or a Pr-doped langasite buffer layer deposited on a material of the group comprising at least one of Si, Al₂O₃, Ge, or similar materials.
 13. The method of claim 7, wherein the phosphor-doped (a)-langasite layer comprises the formula La_(3-x-y)Ce_(x)Pr_(y)Ga₅SiO₁₄ (x=0.1±3%, y=0.01±1%).
 14. The method of claim 1, wherein the phosphor-doped (a)-langasite layer comprises the formula La_(3-x-y)Ce_(x)Pr_(y)Ga₅SiO₁₄ (x=0.1±3%, y=0.01±1%). 